JEFFCO 3110
2:1 FAST CURING HARDENER
Back to
Hardener page
Product Description:
Aliphatic polyamine hardener blend. Fast curing agent designed for impact resistance in damp or humid environments. Low viscosity. Easy to use 2:1 mix ratio (43 by weight ). No VOC’s, 100% solids.
Product Uses:
Crack injection, bonding adhesives, chemically resistant patching compounds, fast setting primers, small castings, surface coatings and thin cross section laminates. May be blended with other 2:1 systems as an accelerator. |
| PROPERTIES OF 3110 HARDENER (neat): |
Minimum |
Maximum |
| Gel Time: Gel Time (minutes@ 77°F, 150 grams)
|
6
|
9
|
| Viscosity: @ 77°F, cps
|
200
|
400
|
|
Color: (Gardener)
|
3
|
|
Weight Per Gallon: (lbs.)
|
8.0
|
8.0
|
|
Weight Per Active H:
|
94 |
94 |
|
Mix Ratio: Parts Per 100 Resin (by weight, 2:1 volume)
|
43
|
43
|
|
Thin Film Cure Time: (minutes @ 175°F)
|
|
|
|
Thin Film Set Time: @ 77°F (hours)
|
2
|
2
|
|
Cure Time: @ 75°F (hours)
|
|
|
|
Pot Life: (minutes @ 77°F, 150 grams)
|
|
|
|
TYPICAL CURED PROPERTIES WITH 1301, 1303, 1308-NC
RESINS
|
Minimum |
Maximum |
|
Cure schedule: Gel @ ambient + 2 hours @ 212°F or 7 days at 77°F
|
|
HDT: (°F) ASTM D648-264
|
147
|
147
|
|
Shore D Hardness:
|
80
|
80
|
|
Barcol Hardness Units :
|
|
|
|
Flexural Strength: (psi)
|
15,870
|
15,870
|
|
Flexural Modulus: (psi)
|
-
|
|
|
Tensile Strength: (psi)
|
9,500
|
9,500
|
|
Tensile Modulus: (psi)
|
-
|
|
|
Elongation: %
|
3.5
|
3.5
|
|
Compressive Strength: (psi)
|
|
|
|
Bond Strength: psi ASTM C882
|
|
|
|
Water Absorption: %
|
|
|
|
Heat Deflection Temperature:
|
|
|
|
Heat Distortion Temperature: °C
|
|
|
|
Service Temperature: °F
|
|
|
|
Tensile Strain at Break: %
|
|
|
|
How Supplied:
Gallons, Pails, Drums
Back to
Hardener page
The information contained herein is offered without charge
for use by technically qualified personnel at their discretion and risk.
All statements, technical information and recommendations contained herein
are based on test and data which we believe to be reliable, but the accuracy
or completeness thereof is not guaranteed and no warranty of any kind
is made with respect thereto. Always read, understand, and comply with
hazard warnings described in the products' Material Safety Data Sheet(s)
before use.
|