JEFFCO 3141
FAST 4:1 PRESS MOLDING HARDENER
Back to
Hardener page
Product Description:
Aliphatic polyamine blend. Fast curing, very low viscosity hardener designed for impact resistance and mold cycling speed. 4:1 volumetric mix ratio. No VOC’s, 100% solids.
Product Uses:
Press molded parts such as snow-skis, water-skis, snowboards, etc.
|
| PROPERTIES OF 3141 HARDENER (neat): |
Minimum |
Maximum |
| Gel Time: Gel Time (minutes@ 77°F, 150 grams) |
10
|
15
|
| Viscosity: @ 77°F, cps
|
100
|
200
|
|
Color: (Gardener)
|
2 |
|
Weight Per Gallon: (lbs.)
|
8.2
|
8.2
|
|
Weight Per Active H:
|
|
|
|
Mix Ratio: PHR 100 Resin (by weight, 4:1 volume)
|
22 |
22 |
|
Thin Film Cure Time: (minutes @ 175°F)
|
|
|
|
Thin Film Set Time: @ 175°F (minutes)
|
4
|
8
|
|
Cure Time: @ 75°F (hours)
|
|
|
|
Pot Life: (minutes @ 77°F, 150 grams)
|
|
|
|
TYPICAL CURED PROPERTIES WITH 1301 RESIN
|
Minimum |
Maximum |
|
Cure schedule: Gel @ ambient + 2 hours @ 212° F or 7 days at 77° F
|
|
HDT: (°F) ASTM D648-264
|
195
|
195
|
|
Shore D Hardness:
|
85
|
85
|
|
Barcol Hardness Units :
|
|
|
|
Flexural Strength: (psi)
|
17,870
|
17,870
|
|
Flexural Modulus: (psi)
|
|
|
|
Tensile Strength:
|
9,500
|
9,500
|
|
Tensile Modulus: (psi)
|
|
|
|
Elongation: %
|
5
|
5
|
|
Compressive Strength: (psi)
|
|
|
|
Bond Strength: psi ASTM C882
|
|
|
|
Water Absorption: %
|
|
|
|
Heat Deflection Temperature:
|
|
|
|
Heat Distortion Temperature: °C
|
|
|
|
Service Temperature: °F
|
|
|
|
Tensile Strain at Break: %
|
|
|
|
|
How Supplied:
Gallons, Pails, Drums
Back to
Hardener page
The information contained herein is offered without charge
for use by technically qualified personnel at their discretion and risk.
All statements, technical information and recommendations contained herein
are based on test and data which we believe to be reliable, but the accuracy
or completeness thereof is not guaranteed and no warranty of any kind
is made with respect thereto. Always read, understand, and comply with
hazard warnings described in the products' Material Safety Data Sheet(s)
before use.
|