JEFFCO 3153
HIGH TEMP LAMINATING HARDENER
Back to
Hardener page
Product Description:
Cycloaliphatic/aliphatic amine blend. Room
temperature cure with heat deflection temperature of 190° F and service
temperature of 225° F attainable with elevated post-curing. Very low
viscosity. Excellent chemical resistance. 100:22 PHR mix ratio. No VOC’s,
100% solids.
Product Uses:
Hand lay up laminating, tooling and press molded parts.
|
| PROPERTIES OF 3153 HARDENER (neat): |
Minimum |
Maximum |
| Gel Time: Gel Time (minutes@ 77°F, 150 grams)
|
25
|
30
|
| Viscosity: @ 77°F, cps
|
150
|
175
|
|
Color: (Gardener)
|
2
|
|
Weight Per Gallon: (lbs.)
|
8.4
|
8.4
|
|
Weight Per Active H:
|
|
|
|
Mix Ratio: Parts Per 100 Resin (by weight, 4:1 volume)
|
22 |
22 |
|
Thin Film Cure Time: (minutes @ 175°F)
|
|
|
|
Thin Film Set Time: @ 77°F (hours)
|
4.5
|
4.5
|
|
Cure Time: @ 75°F (hours)
|
|
|
|
Pot Life: (minutes @ 77°F, 150 grams)
|
|
|
|
| TYPICAL CURED PROPERTIES WITH 1301, 1304T, 1310L-6 or 1319 Resins |
Minimum |
Maximum |
|
Cure schedule: Gel @ ambient + 2 hours @ 212° F or 7 days at 77° F
|
|
HDT: (°F) ASTM D648-264
|
190
|
190
|
|
Shore D Hardness:
|
85*
|
85*
|
|
Barcol Hardness Units :
|
|
|
|
Flexural Strength: (psi)
* = Indicates using 8 plies of 7500 glass |
32,000
|
>32,000*
|
|
Flexural Modulus: (psi)
|
|
|
|
Tensile Strength:
|
30,000
|
>30,000*
|
|
Tensile Modulus: (psi)
|
|
|
|
Elongation: %
|
2.5*
|
2.5*
|
|
Compressive Strength: (psi)
|
20,000
|
>20,000*
|
|
Bond Strength: psi ASTM C882
|
|
|
|
Water Absorption: %
|
|
|
|
Heat Deflection Temperature:
|
|
|
|
Heat Distortion Temperature: °C
|
|
|
|
Service Temperature: °F
|
225
|
225
|
|
Tensile Strain at Break: %
|
|
|
|
How Supplied:
Pails, Drums
Back to
Hardener page
The information contained herein is offered without charge
for use by technically qualified personnel at their discretion and risk.
All statements, technical information and recommendations contained herein
are based on test and data which we believe to be reliable, but the accuracy
or completeness thereof is not guaranteed and no warranty of any kind
is made with respect thereto. Always read, understand, and comply with
hazard warnings described in the products' Material Safety Data Sheet(s)
before use.
|