JEFFCO 3154
MEDIUM POT LIFE 4:1 HARDENER
Back to
Hardener page
Product Description:
A
medium pot life hardener for vacuum bagging, RTM, or wet lay up. Long
work life in the laminate, with fast cure response to external heat make
this an ideal vacuum bagging or RTM hardener. Exhibits very low
exudation allowing secondary bonding with minimal preparation. Cured
material has >165°F
HDT without a post cure, improving to over 180°F
with a mild post cure. Easy to use 4:1 volume mix ratio (100:22 by
weight). Very low viscosity (50-75 cps neat), allows use with many
different JEFFCO Resins. Low odor, no VOC’s, 100% solids.
Product Uses:
Composite parts made by hand lay up, RTM, vacuum bagging, or infusion.
|
| PROPERTIES OF 3154 HARDENER (neat): |
Minimum |
Maximum |
| Gel Time: Gel Time (minutes@ 77°F, 150 grams)
|
40
|
45
|
| Viscosity: @ 77°F, cps
|
50
|
75
|
|
Color: (Gardener)
|
|
|
Weight Per Gallon: (lbs.)
|
|
|
|
Weight Per Active H:
|
|
|
|
Mix Ratio: Parts Per 100 Resin (by weight, 4:1 volume)
|
|
|
|
Thin Film Cure Time: (minutes @ 175°F)
|
|
|
|
Thin Film Set Time: @ 75°F (hours)
|
6.5
|
6.5
|
|
Cure Time: @ 75°F (hours)
|
14 |
16 |
|
Pot Life: (minutes @ 77°F, 150 grams)
|
|
|
|
| TYPICAL CURED PROPERTIES WITH 1310-L6 |
Minimum |
Maximum |
|
Cure schedule: Gel @ ambient + 2 hours @ 212° F or 7 days at 77° F
|
|
HDT: (°F) ASTM D648-264
|
185
|
185 |
|
Shore D Hardness:
|
80 |
80 |
|
Barcol Hardness Units :
|
|
|
|
Flexural Strength: (psi)
|
|
|
|
Flexural Modulus: (psi)
|
|
|
|
Tensile Strength:
|
|
|
|
Tensile Modulus: (psi)
|
|
|
|
Elongation: %
|
|
|
|
Compressive Strength: (psi)
|
|
|
|
Bond Strength: psi ASTM C882
|
|
|
|
Water Absorption: %
|
|
|
|
Heat Deflection Temperature:
|
|
|
|
Heat Distortion Temperature: °C
|
|
|
|
Service Temperature: °F
|
|
|
|
Tensile Strain at Break: %
|
|
|
|
How Supplied:
Pails, Drums
Back to
Hardener page
The information contained herein is offered without charge
for use by technically qualified personnel at their discretion and risk.
All statements, technical information and recommendations contained herein
are based on test and data which we believe to be reliable, but the accuracy
or completeness thereof is not guaranteed and no warranty of any kind
is made with respect thereto. Always read, understand, and comply with
hazard warnings described in the products' Material Safety Data Sheet(s)
before use.
|