JEFFCO 3179
50 MINUTE 4:1 HARDENER
Back to
Hardener page
Product Description:
A minimum toxicity laminating hardener for use on large parts. Exhibits very low exudation allowing for secondary bonding with minimal preparation. Low odor and low to moderate skin toxicity for wet lay up laminating. Cured material has >185°F HDT without a post cure allowing finished laminate to be used elevated service environments. Easy to use 4:1 volume (100:22 by weight) mix ratio. 100% solids, zero VOC’s and ships DOT non-regulated.
Product Uses:
Composite parts and tooling made by hand lay up and vacuum bagging.
|
| PROPERTIES OF 3179 HARDENER (neat): |
Minimum |
Maximum |
| Gel Time: Gel Time (minutes@ 77°F, 150 grams)
|
45
|
55
|
| Viscosity: @ 77°F, cps
|
250
|
300
|
|
Color: (Gardener)
|
4+
|
|
Weight Per Gallon: (lbs.)
|
8.2
|
8.2
|
|
Weight Per Active H:
|
|
|
|
Mix Ratio: Parts Per 100 Resin (by weight, 4:1 volume)
|
22
|
22
|
|
Thin Film Cure Time: (minutes @ 175°F)
|
|
|
|
Thin Film Set Time: @ 77°F (hours)
|
6 |
6.5 |
|
Cure Time: @ 75°F (hours)
|
|
|
|
Pot Life: (minutes @ 77°F, 150 grams)
|
|
|
|
TYPICAL CURED PROPERTIES WITH 1379 RESIN
|
Minimum |
Maximum |
|
CURED PHYSICAL PROPERTIES (1 ply 34 oz biaxial, 1 ply 26 oz unidirectional, 65% glass)
|
|
HDT: (°F) ASTM D648-264
|
|
|
|
Shore D Hardness:
|
88 |
88 |
|
Barcol Hardness Units :
|
|
|
|
Flexural Strength: (psi) D-790
|
17,560
|
17,560
|
|
Flexural Modulus: (psi) D-790 x 10 to the 6th power
|
419,100
|
419,100
|
|
Tensile Strength: (psi) D-638
|
9,544
|
9,544
|
|
Tensile Modulus: (psi) x 10 to the 6th power
|
451,700
|
451,700
|
|
Elongation: %
|
3.97 |
3.97 |
|
Compressive Strength: (psi)
|
|
|
|
Bond Strength: (psi) ASTM C882
|
|
|
|
Water Absorption: %
|
.14
|
.14
|
|
Heat Deflection Temperature:
|
|
|
|
Heat Distortion Temperature: °C
|
|
|
|
Service Temperature: °F
|
|
|
|
Tensile Strain at Break: %
|
|
|
|
How Supplied:
Pails, Drums, Tote Bin
Back to
Hardener page
The information contained herein is offered without charge
for use by technically qualified personnel at their discretion and risk.
All statements, technical information and recommendations contained herein
are based on test and data which we believe to be reliable, but the accuracy
or completeness thereof is not guaranteed and no warranty of any kind
is made with respect thereto. Always read, understand, and comply with
hazard warnings described in the products' Material Safety Data Sheet(s)
before use.
|