JEFFCO 3181
SAFETY 3:1 LAMINATING HARDENER
Back to
Hardener page
Product Description:
Modified polyamide/polyamine hardener. 30 minute pot life, with fast cycle times at standard process temperatures. Excellent bonding to difficult substrates. Fast wetting of fiberglass reinforcements. Good workability with carbon and KevlarÔ fabrics. Easy to use 3:1 volumetric mix ratio. A good all-around tooling and laminating hardener. Low toxicity, low odor system. No VOC’s, 100% solids. Ships DOT non-regulated.
Product Uses:
Composite parts and tools made by hand lay-up, vacuum bag or other molding techniques |
| PROPERTIES OF 3181 HARDENER (neat): |
Minimum |
Maximum |
| Gel Time: Gel Time (minutes@ 77°F, 100 grams)
|
25
|
35
|
| Viscosity: @ 77°F, cps
|
350
|
550
|
|
Color: (Gardener)
|
4
|
|
Weight Per Gallon: (lbs.)
|
8.3
|
8.3
|
|
Weight Per Active H:
|
|
|
|
Mix Ratio: Parts Per 100 Resin (by weight, 3:1 volume)
|
29
|
29
|
|
Thin Film Cure Time: (minutes @ 175°F)
|
|
|
|
Thin Film Set Time: @ 77°F (hours)
|
15
|
20
|
|
Cure Time: @ 75°F (hours)
|
|
|
|
Pot Life: (minutes @ 77°F, 100 grams)
|
|
|
|
TYPICAL CURED PROPERTIES WITH JEFFCO 1381-R-1 Resin
|
Minimum |
Maximum |
|
Cure schedule: Gel @ ambient + 2 hours @ 212°F or 7 days @ 77°F
|
|
HDT: (°F) ASTM D648-264
|
185
|
185
|
|
Shore D Hardness:
|
85
|
85
|
|
Barcol Hardness Units :
|
|
|
|
Flexural Strength: (psi)
|
18,560
|
18,560
|
|
Flexural Modulus: (psi)
|
|
|
|
Tensile Strength: (psi)
|
9,750
|
9,750
|
|
Tensile Modulus: (psi)
|
|
|
|
Elongation: %
|
4.5
|
4.5
|
|
Compressive Strength: (psi)
|
|
|
|
Bond Strength: (psi) ASTM C882
|
|
|
|
Water Absorption: %
|
|
|
|
Heat Deflection Temperature:
|
|
|
|
Heat Distortion Temperature: °C
|
|
|
|
Service Temperature: °F
|
|
|
|
Tensile Strain at Break: %
|
|
|
|
How Supplied:
Pails, Drums
Back to
Hardener page
The information contained herein is offered without charge
for use by technically qualified personnel at their discretion and risk.
All statements, technical information and recommendations contained herein
are based on test and data which we believe to be reliable, but the accuracy
or completeness thereof is not guaranteed and no warranty of any kind
is made with respect thereto. Always read, understand, and comply with
hazard warnings described in the products' Material Safety Data Sheet(s)
before use.
|