JEFFCO 4109-R1
EPOXY HARDENER
Back to
Hardener page
Product Description:
Modified amine hardener. 40-minute pot life, with fast cure times at standard process temperatures. Excellent bonding to difficult substrates. Fast wetting of fiberglass reinforcements. Very low color and excellent clarity. Easy to use 2:1 mix ratio. Low-toxicity, low-odor system. No VOC’s, 100% solids.
Product Uses:
Composite filament wound parts, hand lay-up laminating, clear protective coatings. Excellent general purpose 2:1 hardener. |
| PROPERTIES OF 4109-R1 HARDENER (neat): |
Minimum |
Maximum |
| Gel Time: (minutes @ 77° F, 150 grams)
|
35
|
40
|
| Viscosity: @ 77°F, cps
|
150
|
250
|
|
Color: (Gardener)
|
<2 |
|
Weight Per Gallon: (lbs.)
|
8.3 |
8.5 |
|
Weight Per Active H:
|
|
|
|
Mix Ratio: Parts Per 100 Resin (by weight, 100:56 by volume
with 1409-R2)
|
50 |
50 |
|
Thin Film Cure Time: (minutes @ 175°F)
|
|
|
|
Thin Film Set Time: @ 90°F (hours)
|
<3
|
3
|
|
Cure Time: @ 90°F (hours)
|
12
|
12
|
|
Pot Life: (minutes @ 77°F, 150 grams)
|
|
|
|
TYPICAL CURED PROPERTIES WITH 1409-R2 RESIN
|
Minimum |
Maximum |
|
Cure schedule: Gel @ ambient + 12 hours @ 90° F or 7 days at
ambient
|
|
HDT: (°F) ASTM D648-264
|
170
|
170
|
|
Shore D Hardness:
|
85 |
85 |
|
Barcol Hardness Units :
|
|
|
|
Flexural Strength: (psi)
|
15,530 |
15,530 |
|
Flexural Modulus: (psi)
|
|
|
|
Tensile Strength: (psi)
|
9,750 |
9,750 |
|
Tensile Modulus: (psi)
|
|
|
|
Elongation: %
|
5 |
5 |
|
Compressive Strength: (psi)
|
|
|
|
Bond Strength: psi ASTM C882
|
|
|
|
Water Absorption: %
|
|
|
|
Heat Deflection Temperature:
|
|
|
|
Heat Distortion Temperature: °C
|
|
|
|
Service Temperature: °F
|
|
|
|
Tensile Strain at Break: %
|
|
|
|
How Supplied:
Pails, Drums, Tote Bin
Back to
Hardener page
The information contained herein is offered without charge
for use by technically qualified personnel at their discretion and risk.
All statements, technical information and recommendations contained herein
are based on test and data which we believe to be reliable, but the accuracy
or completeness thereof is not guaranteed and no warranty of any kind
is made with respect thereto. Always read, understand, and comply with
hazard warnings described in the products' Material Safety Data Sheet(s)
before use.
|