JEFFCO 4300
PRESS MOLDING HARDENER
Back to
Hardener page
Product Description:
Low-viscosity aliphatic amine hardener. Fast setting, even in thin films with high HDT and excellent chemical resistance. Cures at ambient or elevated temperatures. Economical with easy to use mix ratio. Very versatile, 100% solids curing agent.
Product Uses:
Press-molding, hand lay-up laminating, tooling, construction adhesives, chemically resistant flooring, and as an accelerator for other curing agents.
|
| PROPERTIES OF 4300 HARDENER (neat): |
Minimum |
Maximum |
| Gel Time: minutes (150 grams)
|
12
|
15
|
| Viscosity: @ 77°F, cps
|
85
|
125
|
|
Color: (Gardener)
|
2 |
|
Weight Per Gallon: (lbs.)
|
8.6 |
8.6 |
|
Weight Per Active H:
|
30 |
30 |
|
Mix Ratio: Parts Per 100 Resin (by weight, 5:1 volume)
|
16 PHR |
|
|
Thin Film Cure Time: (minutes @ 175°F)
|
|
|
|
Thin Film Set Time: @ 75°F (hours)
(8-10 minutes @ 175°F) |
2 |
2 |
|
Cure Time: @ 75°F (hours)
|
|
|
|
Pot Life: (minutes @ 77°F, 150 grams)
|
|
|
|
TYPICAL CURED PROPERTIES WITH 1301 RESIN
|
Minimum |
Maximum |
|
Cure schedule: Gel @ ambient + 2 hours @ 175° F or 7 days at
77° F |
|
HDT: (°F) ASTM D648-264
|
200
|
200
|
|
Shore D Hardness:
|
82 |
82 |
|
Barcol Hardness Units :
|
|
|
|
Flexural Strength: (psi)
|
14,650 |
14,650 |
|
Flexural Modulus: (psi)
|
355,000 |
355,000 |
|
Tensile Strength: (psi)
|
7,500 |
7,500 |
|
Tensile Modulus: (psi)
|
|
|
|
Elongation: %
|
3.8 |
3.8 |
|
Compressive Strength: (psi)
|
|
|
|
Bond Strength: psi (mild steel to mild steel)
|
1,650 |
1,650 |
|
Water Absorption: %
|
|
|
|
Heat Deflection Temperature:
|
|
|
|
Heat Distortion Temperature: °C
|
|
|
|
Service Temperature: °F
|
|
|
|
Tensile Strain at Break: %
|
|
|
|
How Supplied:
Pails, Drums
Back to
Hardener page
The information contained herein is offered without charge
for use by technically qualified personnel at their discretion and risk.
All statements, technical information and recommendations contained herein
are based on test and data which we believe to be reliable, but the accuracy
or completeness thereof is not guaranteed and no warranty of any kind
is made with respect thereto. Always read, understand, and comply with
hazard warnings described in the products' Material Safety Data Sheet(s)
before use.
|